Influence of the dipolar interactions in the magnetization reversal asymmetry of hard-soft magnetic ribbons
|
Autor/a:
|
Rivas Ardisana, Montserrat; García Díaz, José Ángel; Tejedor Gancedo, Marcos; Bertrán Serra, Enric; Céspedes, J. G.
|
Otros autores:
|
Universitat de Barcelona |
Abstract:
|
Partial crystallization of the metallic glass Co66Si16B12Fe4Mo2 was performed by annealing at temperatures between 500 and 540°C for 10-20 min, resulting in crystallite volume fractions of (0.7-5)×10¿3 and sizes of 50-100 nm. This two-phase alloy presents a remarkable feature: a hysteresis loop shift that can be tailored by simply premagnetizing the sample in the adequate magnetic field. Shifts as large as five times the coercive field have been obtained which make them interesting for application as magnetic cores in dc pulse transformers. The asymetrical magnetic reversal is explained in terms of the magnetic dipolar field interaction and the observed hysteresis loops have been satisfactorily simulated by a modification of Stoner-Wohlfarth¿s model of coherent rotations. |
Materia(s):
|
-Ferromagnetisme -Anisotropia -Magnetisme -Nanocristalls -Propietats magnètiques -Microscòpia electrònica -Histèresi -Ferromagnetism -Anisotropy -Magnetism -Nanocrystals -Magnetic properties -Electron microscopy -Hysteresis |
Derechos:
|
(c) American Institute of Physics, 2005
|
Tipo de documento:
|
Artículo Artículo - Versión publicada |
Editor:
|
American Institute of Physics
|
Compartir:
|
|