Title:
|
Polyterephthalates made from ethylene glycol, 1,4-cyclohexanedimethanol, and isosorbide
|
Author:
|
Quintana Vicente, Robert; Martínez de Ilarduya Sáez de Asteasu, Domingo Antxon; Alla Bedahnane, Abdelilah; Muñoz Guerra, Sebastián
|
Other authors:
|
Universitat Politècnica de Catalunya. Departament d'Enginyeria Química; Universitat Politècnica de Catalunya. POL - Polímers Industrials Avançats i Biopolímers Tecnològics |
Abstract:
|
Three series of terephthalate polyesters (copolyesters and terpolyesters) containing 70, 80, and 90 mol % of ethylene glycol respectively, 1,4-cyclohexanedimethanol (CHDM) and isosorbide in varying ratios, were synthesized by melt polycondensation.
It was found that only ~75 mol % of the feeding isosorbide was incorporated in the resulting polyesters and that their content in diethylene glycol oscillated between 2 and
4 mol %. The polyesters had weight-average molecular weights in the 25,000–33,000 g mol~1 range and polydispersities between 2 and 2.5. The combined 1H and 13C NMR analysis
revealed that the microstructure of all these polyesters was at random. They showed good thermal stability with decomposition
temperatures above 400ºC. Their glass-transition temperatures were observed to increase with the content in cyclic
diols, this effect being more pronounced when isosorbide was the replacing comonomer. Only the series containing 90 mol% of ethylene terephthalate units was able to crystallize upon cooling from the melt. Compared isothermal crystallizations
revealed that isosorbide was more effective than CHDM in repressing the crystallizability of PET. |
Abstract:
|
Peer Reviewed |
Subject(s):
|
-Àrees temàtiques de la UPC::Enginyeria dels materials::Materials plàstics i polímers -Copolymers -- Thermal properties -Copolímers |