Lead-free (K,Na)NbO3 (KNN) and La doped (K,Na)NbO3 (KNN-La) thin films are grown on SrTiO3 substrates using the chemical solution deposition method. The effect of adding different amounts of Na and K excess (0-20 mol%) is investigated. The results confirm the necessity of adding 20 mol% excess amounts of Na and K precursor solutions in order to avoid the formation of the secondary phase, K4Nb6O17, as confirmed by X-ray diffraction and Raman spectroscopy. Moreover, when adding a 20 mol% of alkaline metal excess, the thin films are highly textured with out-of-plane preferential orientation in the [100] direction of the [100] orientation of the substrate. Doping with lanthanum results in a decrease of the leakage current density at low electric field, and an increase in the dielectric permittivity across the whole temperature range (80-380 K). Although the (100)-oriented KNN and KNN-La films exhibited rounded hysteresis loops, at low temperatures the films show the typical ferroelectric hysteresis loops. (C) 2015 Elsevier B.V. All rights reserved.