The present study is focused on analyzing the effect of Mn amount on two experimental steel compositions, specially designed for Q&P (Quenching and Partitioning), 0.15C-2.5Mn-1.5Si and 0.15C-3Mn-1.5Si without significant contribution of Al. Two-Step Q&P thermal treatments were performed at laboratory scale in a quenching dilatometer Bähr DIL805A/D. The fractions of retained austenite were evaluated by X-ray diffraction techniques. The mechanical properties of the Q&P samples were evaluated, a strong dependence of strength, uniform elongation and strain hardening values on process parameters has been found. Higher uniform elongation were related to higher residual austenite contents. The 0.15C-3Mn-1.5Si steel showed systematically the largest mechanical values with respect to the 0.15C-2.5Mn-1.5Si steel.