Title:
|
Influence of hydrothermal degradation on wear behaviour of Zirconia tetragonal polycrystals doped with 3% molar of yttria
|
Author:
|
Kiran Chitapalli, Ravi; Valle Chiro, Jorge Antonio; Mestra Rodríguez, Álvaro Miguel; Anglada Gomila, Marcos Juan
|
Other authors:
|
Universitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica; Universitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural, Micromecànica i Fiabilitat dels Materials |
Abstract:
|
The goal of this work is to analyse the influence of hydrothermal degradation on wear behaviour on samples of tetragonal polycrystals doped with 3% molar of yttria in air under dry sliding conditions on samples artificially aged at 0, 10 and 60 hours in autoclave at 131°C. The samples were prepared by conventional compaction and sintering at 1450°C. The study was carried out by performing scratch tests and ball on disc experiments against 3Y-TZP balls. At low
loads the damage was not distinctive, but under high loads the damage mechanisms were different suggesting a clear effect of degradation after long ageing times. On the contrary, in samples degraded during 60 hours the wear rates in both experiments were initially higher than on non-aged specimens and decreased with increasing load and/or sliding distance. |
Abstract:
|
Peer Reviewed |
Subject(s):
|
-Àrees temàtiques de la UPC::Enginyeria dels materials::Assaig de materials -Hydrotermal degradation -Zirconia doped with yttria -Zircó |