Título: | Corrosion damage in WC-Co cemented carbides: Residual strength assessment and 3D FIB-FESEM tomography characterization |
---|---|
Autor/a: | Tarragó Cifre, Jose María; Fargas Ribas, Gemma; Jiménez Piqué, Emilio; Felip, Alba; Isern, Lluis; Coureaux Mustelier, David; Al-Dawery, Ihsan; Roa Rovira, Joan Josep; Fair, Jonathan; Llanes Pitarch, Luis Miguel |
Otros autores: | Universitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica; Universitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural, Micromecànica i Fiabilitat dels Materials |
Abstract: | The effect of corrosion damage on cemented carbides was investigated. The study included residual strength assessment and detailed fractographic inspection of corroded specimens as well as detailed 3D FIB-FESEM tomography characterization. Experimental results point out a strong strength decrease associated with localized corrosion damage, i.e. corrosion pits acting as stress raisers, concentrated in the binder phase. These pits exhibit a variable and partial interconnectivity, as a function of depth from the surface, and are the result of heterogeneous dissolution of the metallic phase, specifically at the corrosion front. However, as corrosion advances the ratio between pit depth and thickness of damaged layer decreases. Thus, stress concentration effect ascribed to corrosion pits gets geometrically lessened, damage becomes effectively homogenized and relatively changes in residual strength as exposure time gets longer are found to be less pronounced. |
Materia(s): | -Àrees temàtiques de la UPC::Enginyeria dels materials -Cement composites -Carbides -Corrosion -Cemented carbides -Residual strength -FIB Tomography -Aliatges de carbur de tungstè i cobalt -Materials ceràmics -- Corrosió -Carburs |
Derechos: | Attribution-NonCommercial-NoDerivs 3.0 Spain
http://creativecommons.org/licenses/by-nc-nd/3.0/es/ |
Tipo de documento: | Artículo - Versión publicada Objeto de conferencia |
Compartir: |