Al-3Mg alloy reinforced with B4C particles in volume fractions of 5, 10 and 15% were subjected to hot deformation to investigate the impact of presence of ceramic particles and deformation condition on final texture. Single-heat hot compression test was performed at temperatures of 300–500¿°C with strain rates of 10-3 to 10 s-1. The electron backscatter diffraction method was applied to evaluate the final texture and microstructures. It was observed that the {110} fiber formed during deformation was intensified by increasing the Zenner-Holloman parameter, while deformation at lower Z makes {100} fiber pervasive throughout the matrix. Developing {100} fiber in such condition leads to continual softening of flow stress. Presence of particles by promoting particle stimulating nucleation mechanism at high Z and restricting grains rotation at low Z led to lower final texture intensity.