Surface modification of TiO₂ nanocrystals by WOx coating or wrapping : solvothermal synthesis and enhanced surface chemistry
|
Autor/a:
|
Epifani, Mauro; Díaz, Raül; Force, Carmen; Comini, Elisabetta; Manzanares, Marta; Andreu, Teresa; Genç, Aziz; Arbiol i Cobos, Jordi; Siciliano, Pietro; Faglia, Guido; Morante, Joan Ramon
|
Abstract:
|
Ajuts: CSIC/CNR project 2010IT0001 (SYNCAMON), SOLAR project DM19447. JA and AZ acknowledge ICN2 Severo Ochoa Excellence Grant |
Abstract:
|
TiO₂ anatase nanocrystals were prepared by solvothermal processing of Ti chloroalkoxide in oleic acid, in the presence of W chloroalkoxide, with W/Ti nominal atomic concentration (Rw) ranging from 0.16 to 0.64. The as-prepared materials were heat-treated up to 500 °C for thermal stabilization and sensing device processing. For R₀.₁₆, the as-prepared materials were constituted by an anatase core surface-modified by WOₓ monolayers. This structure persisted up to 500 °C, without any WO₃ phase segregation. For Rw up to R₀.₆₄, the anatase core was initially wrapped by an amorphous WOₓ gel. Upon heat treatment, the WOₓ phase underwent structural reorganization, remaining amorphous up to 400 °C and forming tiny WO₃ nanocrystals dispersed into the TiO₂ host after heating at 500 °C, when part of tungsten also migrated into the TiO₂ structure, resulting in structural and electrical modification of the anatase host. The ethanol sensing properties of the various materials were tested and compared with pure TiO₂ and WO₃ analogously prepared. They showed that even the simple surface modification of the TiO₂ host resulted in a 3 orders of magnitude response improvement with respect to pure TiO₂. |
Materia(s):
|
-Gas sensors -Metal oxide nanocrystals -Nanocomposites -Solvothermal synthesis -Surface modification -TiO₂ |
Derechos:
|
open access
Tots els drets reservats.
https://rightsstatements.org/vocab/InC/1.0/ |
Tipo de documento:
|
Article |
Editor:
|
|
Compartir:
|
|
Uri:
|
https://ddd.uab.cat/record/200199
|