Solution deposited YBaCuO (YBCO) nanocomposites with preformed nanoparticles represent a promising cost-effective approach for superior critical current properties under applied magnetic fields. Nonetheless, the majority of YBCO nanocomposites with high nanoparticle loads (>20%) suffer from nanoparticle coalescence and degraded superconducting properties. Here, we study the influence of nanoparticle concentration (0-25% mol), size (5 nm-10 nm) and composition (BaHfO, BaZrO) on the generation of structural defects in the epitaxial YBCO matrix, key parameter for vortex pinning. We demonstrate that flash-heated superconducting nanocomposites with 20 mol% preformed BaHfO or BaZrO perovskite secondary phases feature discrete and small (7 nm) nanoparticles and high density of YBaCuO (Y248) intergrowths. We identify a synergy between Y248 intergrowth density and small nanoparticles to increase artificial vortex pinning centers. Also, we validate the multideposition process to successfully increase film thickness of epitaxial nanocomposites with competitive critical currents I at 77 K.