Universitat Autònoma de Barcelona
We have grown high quality magnetite microcrystals free from antiphase boundaries on Ru(0001) by reactive molecular beam epitaxy, conserving bulk magnetic properties below 20 nm thickness. Magnetization vector maps are obtained by X-ray spectromicroscopy and compared with micromagnetic simulations. The observed domain configurations are dictated purely by shape anisotropy, overcoming the possible influences of (magneto)crystalline anisotropy and defects, thus demonstrating the possibility of designing spin structures in ultrathin, magnetically soft magnetite at will.
Anglès
Antiphase boundaries; Crystalline anisotropy; Domain configurations; Magnetite microcrystals; Magnetization vector; Micromagnetic simulations; Shape anisotropy; X-ray spectromicroscopy
Ministerio de Economía y Competitividad MAT2013-48009-C4-1-P
Ministerio de Economía y Competitividad MAT2014-52477-C5-2-P
Ministerio de Economía y Competitividad MAT2015-64110-C2-1-P
Ministerio de Economía y Competitividad MAT2015-64110-C2-2-P
European Commission 720853
European Commission 696656
Nanoscale ; Vol. 10, Issue 12 (March 2018), p. 5566-5573