Impact of supporting electrolyte on electrochemical performance of borophene-functionalized graphene sponge anode and degradation of per- and polyfluoroalkyl substances (PFAS)

Abstract

Graphene sponge anode functionalized with two-dimensional (2D) boron, i.e., borophene, was applied for electrochemical oxidation of C4-C8 per- and polyfluoroalkyl substances (PFASs). Borophene-doped graphene sponge outperformed boron-doped graphene sponge anode in terms of PFASs removal efficiencies and their electrochemical degradation; whereas at the boron-doped graphene sponge anode up to 35% of the removed PFASs was recovered after the current was switched off, the switch to a 2D boron enabled further degradation of the electrosorbed PFASs. Borophene-doped graphene sponge anode achieved 32–77% removal of C4-C8 PFASs in one-pass flow-through mode from a 10 mM phosphate buffer at 230 A m−2 of anodic current density. Higher molarity phosphate buffer (100 mM) resulted in lower PFASs removal efficiencies (11–60%) due to the higher resistance of the graphene sponge electrode in the presence of phosphate ions, as demonstrated by the electrochemical impedance spectroscopy (EIS) analyses. Electro-oxidation of PFASs was more efficient in landfill leachate despite its high organic loading, with up to 95% and 75% removal obtained for perfluorooctane sulfonate (PFOS) and perfluorooctanoic acid (PFOA), versus 77% and 57% removal in the 10 mM phosphate buffer, respectively. Defluorination efficiencies as determined relative to the electrooxidized fraction of PFASs indicated up to 69% and 82% of defluorination of PFOS and PFOA in 10 mM phosphate buffer, which was decreased to 16 and 29% defluorination, respectively, for higher buffer molarity (100 mM) due to the worsened electrochemical performance of the sponge. In landfill leachate, relative defluorination efficiencies of PFOS and PFOA were 33% and 45%, respectively, indicating the inhibiting effect of complex organic and inorganic matrix of landfill leachate on the C-F bond breakage. This study demonstrates that electrochemical degradation of PFASs is possible to achieve in complex and brackish streams using a low-cost graphene sponge anode, without forming toxic chlorinated byproducts even in the presence of >7 g L−1 of chloride

The authors would like to acknowledge ERC Starting Grant project ELECTRON4WATER (grant number 714177). ICRA researchers thank funding from CERCA program. Moreover, the authors acknowledge the support from the Economy and Knowledge Department of the Catalan Government through a Consolidated Research Group (ICRA-TECH - 2021 SGR 01283).

6