Strain tuned magnetoelectric coupling in orthorhombic YMnO3 thin films

Abstract

This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics.

Orthorhombic YMnO3epitaxialthin films were grown on Nb(0.5%)-doped SrTiO3(001) substrates. Film's thickness was varied to tune the epitaxial strain. Structural and magnetic properties are well correlated, presenting a more pronounced ferromagnetic behavior as the unit cell becomes more distorted. Dielectric properties were investigated as a function of the temperature and magnetic field. The dielectric peak occurring at temperatures below the antiferromagnetic ordering is proved to be magnetoelectric and its amplitude is dependent on the unit cell distortion. These findings allow tailoring ferromagnetic and magnetoelectric properties via epitaxial strain.